拉絲鋁板：反復用砂紙將鋁板刮出線條的制造過程，其工藝主要流程分為脫酯、沙磨機、水洗3個部分。在鋁板拉絲制程中，陽極處理之后的特殊的皮膜技術，可以使鋁板表面生成一種含有該金屬成分的皮膜層，清晰顯現每一根細微絲痕，從而使金屬啞光中泛出細密的發絲光澤。
Drawing aluminum sheet: the process of repeated use of sand paper to scrape the aluminum sheet out of the line. The main process is divided into 3 parts: deester, sand mill and water washing. In aluminum wire drawing process, anodized after special coating technology, can make the surface of aluminum to form a coating layer containing the metal component, clear every fine wire mark, so that the pan fine hair gloss matte in metal.
氧化鋁板：將鋁板置于相應電解液(如硫酸、鉻酸、草酸等)中作為陽極，在特定條件和外加電流作用下，進行電解而形成的鋁板。陽極的鋁板氧化，表面上形成氧化鋁薄層，其厚度為5～20微米，硬質陽極氧化膜可達60～200微米。
Aluminum oxide plate: aluminum plate is placed in the corresponding electrolyte (such as sulfuric acid, chromic acid, oxalic acid, etc.) as anode, and the aluminum plate is formed by electrolysis under specific conditions and applied current. The aluminum oxide on the anode forms a thin layer of alumina on the surface, with a thickness of 5~20 microns and a hard anodic oxide film of up to 60~200 microns.
PS鋁板（廣告鋁板又名印刷鋅板、報紙板）：即背面有印刷圖案厚度為025或03料的鋁板。
PS aluminum plate (advertising aluminum plate also known as printed zinc board, newspaper board): the back has a printed pattern thickness of 025 or 03 aluminum plate.
鏡面鋁板：指通過軋延、打磨等多種方法處理，使板材表面呈現鏡面效果的鋁板。
Mirror aluminum sheet: refers to the aluminum plate on the surface of the plate which is treated by various methods such as rolling, grinding and so on.
壓花鋁板又可以稱為鋁壓花板：屬于在鋁板的基礎上，經過壓延加工而在表面形成各種花紋的鋁產品，應用較為廣泛，主要用在包裝，建筑，幕墻等方面鋁卷板屬于鋁材中板材的一種,實際上是長而窄并成卷供應的薄鋁板,

Embossed aluminum and aluminum can be called embossing plate belonging to in the aluminum base, aluminum products after rolling processing and forming on the surface of various patterns, is widely used, mainly used in packaging, building a wall, belonging to the aluminum sheet aluminum coil, is actually a long and narrow and thin aluminum coil supply,
卷和平板差點就是一個裁剪包裝,
The difference between a roll and a flat is a tailored package.
冷硬鋁卷板是熱軋鋁卷板經過酸洗、冷軋得到的.可以說是冷軋板卷的一種.
Cold hard aluminum coils are hot rolled aluminum rolls through pickling and cold rolling. It can be said to be one of the cold rolled sheets.
冷軋板卷(退火態):熱軋鋁卷板經過酸洗、冷軋、罩式退火、平整、(精整)得到的.
Cold rolled sheet (annealed): hot rolled aluminum rolls are obtained through pickling, cold rolling, bell type annealing, leveling, and (finishing).
兩者區別主要有三點:
There are three main differences between the two.
1、外觀上,一般冷硬鋁卷板有點發微烏.
1, the general appearance, a bit cold rolling aluminum micro Ukraine.
2、表面質量、結構、尺寸精度等冷軋板要比冷硬鋁卷板要好.
2, the surface quality, structure, size accuracy and other cold rolled plates are better than cold hard aluminum coils.
3、性能上,由于熱軋鋁卷板經過冷軋工序直接得到的冷硬鋁卷板在冷軋時發生加工硬化,導致屈服強度增加、并殘留了部分內應力,外在表現為較"硬"故稱冷硬鋁卷板.
3, performance, as the hot rolled aluminum coil directly obtained through cold rolling process, the cold hard aluminum coil is hardened during cold rolling, resulting in increased yield strength and residual internal stress. The external performance is "hard", so it is called cold hard aluminum coil.